光泽度分几个等级

RHCM高光过热水模温控制机

RHCM superheated water high-gloss traceless injection mould

急速升降模温技术

Technology of quick rising and drop of mold temperature

传统注塑模具温度控制的不足之处如下

Disadvantages of the traditional temperature control technology for injection molds:

无法满足高光注塑中快速升温及快速降温的需要。

The need of high-gloss injection molding for quick temperature rising and drop cannot be met.

升温幅度较小，制品表面的溶接痕只能得到减轻而无法消除。

The margin of temperature rising is very small. As a result, the welding traces on product surfaces can be alleviated rather than removed thoroughly.

由于塑料硬度越高，流动性越差。因此采用此种工艺，制品表面的硬度只能达到HB级，无法满足实际使用需要。

Due to the great hardness and poor fluidity of plastics, this technology can only make the surface hardness of a product grade HB, failing to meet the actual requirements of application.

模具升温时受热膨胀，降温时又会收缩，使锁模力很不稳定。

Due to the mold’s expansion when in temperature rising and its shrinkage when in temperature drop, the clamping force is quite unstable.

容易造成制品打不满，烧焦、内应力大等各种缺陷。

Thus, the products are easy to suffer from short molding, scorching, excessive internal stress and other defects.

模具的配置

Configuration of die

模具内表面要求非常高的光洁度，以确保制品的表面质量。

The mold’s inner surface should be very smooth, so as to ensure high surface quality for products.

模具内部开设管道必须合理，以确保可以快速升温和降温。

The pipelines arranged in the mold must be rational so that temperature can rise or drop quickly.

模具内部的管道应该导热性能良好。

The mold’s internal pipelines should be of good heat conductivility.

由于生产过程中需要不停加温及降温，模具选用的钢材要好。

The necessity to have temperature rise and drop frequently in production makes it necessary to select good steel materials for the mold.

组织结构均匀，热胀冷缩系数小。

The organizational structure is even and the expansion and shrinkage coefficients are small.

在使用过程中要尤其注重模具的保养，确保干燥、无尘。

Pay special attention to the mold’s maintenance when in use, making it dry and dustless.

GWS应用实例

Cases of GWS application

高光过热水模温控制机优点

Advantages of the superheated water high-gloss mold temperature controller

消除产品表面溶接线，溶接痕，波纹，银丝纹。

Remove the welding wires and traces, ruffles and silver marks on product surfaces.

彻底解决塑料产品的表面缩水现象。

Solve the surface shrinkage of plastic products completely.

提高产品表面光洁度，使表面光洁度可达到镜面。

Enhance the product surface as smooth as a mirror.

产品不需要喷漆后续加工，提高成品率20-30%。

It is unnecessary to conduct processing after spraying to products, increasing the rate of finished products by 20% to 30%.

解决加织产品甩产生的浮织现象使品质更完美。

Solve the float phenomenon of woven products, ensuring better quality.

使薄壁成型提高注塑流动性，提高产品品质和强度。

Make thin walls formed, so as to improve the fluidity in injection molding and product quality and strength.

使厚壁成型注塑周期可降低60%以上，增强塑料的流动性及填充效果。

The injection molding period for the thick wall forming may be reduced by over 60%, improving plastics’ fluidity and filling effect.

95%的热能回收。

95% of heat energy may be recovered.

100%的介质回收。

The medium may be recovered completely.

无需连接锅炉及其他外置温控辅助设备，省略复杂的锅炉设备（高压设备安全和环保的审批）和管道工程。

It is unnecessary to connect it with a boiler or other external auxiliary temperature controlling equipment, avoiding the application of complicated boiler plants (the approval of the safety and environmental protection performance of high-pressure equipment) and pipe works.

完全解决锅炉之蒸汽不可回收的能耗大问题。

Solve the great energy consumption of boilers due to steam cannot be recycled.

体积小可随时移动配合不同机台使用，180℃热水完全代替锅炉的不环保现象。

Due to its small volume, it can be moved conveniently and used with different equipment. The hot water of 180℃ can completely overcome the disadvantage of environmental pollution of boilers.

高光过热水模温控制机特点

Features of superheated water high-gloss traceless injection mould

10.4寸液晶真彩LCD显示（可选），触模式中文数字输入，全中文界面，操作简单。

10.4′truecolor LCD (optional) with touch-type Chinese character input function, all-Chinese interface and simple operations

全闭环系统控制输入输出温度的检测，以模具实际温度反馈PLC，数彩图变化显示，确保输出准确稳定。

A full-closed loop controls the detection of input temperature and output temperaturethe mold’s actual humidity realizes back locking of PLCand digital colors are available for varying display, making the output accurate and stable.

高温热水、冷水，空气温度及压力六项报警，采用时间和温度动作与注塑机信号互锁。

For the six kinds of alarms including high-temperature hot water, cold water, air temperature and pressure, the interlocking between time and temperature movements and the injection molding machine’s signals is employed.

整机采用欧美进口元器件。

Components imported from Europe and USA are used.

单双路模具温度检测（可选），输入输出管道采用316不锈钢管，多组输入输出接口。

A one-way or two-way mold (optional) is used for temperature detectionthe input pipe and the output pipe are made of 316 stainless steel pipesand there are multiple groups of I/O interfaces.

整机配备；加热、冷却、冷热转换控制功能。

The heating, cooling and hot/cold transformation functions are available.

高温热水，冷却水的回收系统，节能效果明显。

It is designed with recovery systems for high-temperature hot water and cooling water, saving energy significantly.

高光过热水模温控制机应用

Application of superheated water high-gloss traceless injection mould

目前在家电、汽车、通讯、日用品、医疗器械等行业具有广泛的应用前景，例如液晶电视机、电脑液晶显示器、笔记本电脑、手机、空调、汽车液晶显示器、汽车内饰件、车灯和光学、OA、AV仪器等行业。

At present, it enjoys extensive application prospects in industries like household electrical appliances, automobiles, communications, articles for daily use, and medical instruments. Particularly, it is widely applied to LCD TV sets, computer LCDs, notebook PCs, mobile phones, air-conditioners, auto LCD, automobile internal ornaments, car lamps, photic, OA and AV instruments, etc.

机器规格

机型 单位 GWS-800 GWS-1600

电源 V 3∮380V/50HZ

总功率 KW 114 157

控制方式 　 电脑PLC处理器+人机界面触摸控制

电热功率 KW 45-108 60-150

加热泵功率 S 2.8 2.8

冷却泵功率 KW 2.2 3.0

冷热水循环却水进出口口径 Inch DN25(3/8x12) DN32(3/8x16)

冷水循环进出口口径 Inch DN32 DN40

外型尺寸 MM 1700x850x1400 1900x900x1600

重量 Kg 700 900

反射光泽度（0-1）0表示物体表面粗糙_1非常光滑，一般是0.8左右（常见材质）

(前提是要有反射或要打开反射)

这两个VRAY里一般都是关联起来的，意思就是光一个材质表面粗糙它的高光面积自然会变大，

比如磨砂塑料就是这样的，然后你试着去把其它材质对比一下它们的这两个属性。

塑料以它优异的性能逐步地代替了许多已经使用了几十年、几百年的材料和器皿，成为人们生活中不可缺少的助手。塑料集金属的坚硬性、木材的轻便性、玻璃的透明性、陶瓷的耐腐蚀性，橡胶的弹性和韧性于一身，因此除了日常用品外，塑料更广泛地应用于航空航天、医疗器械、石油化工、机械制造、国防、建筑等各行各业。

一、塑料的分类

塑料种类很多，到目前为止世界上投入生产的塑料大约有三百多种。塑料的分类方法较多，常用的有两种：

1、根据塑料受热后的性质不同分为热塑性塑料和热固性塑料

热塑性塑料分子结构都是线型结构，在受热时发生软化或熔化，可塑制成一定的形状，冷却后又变硬。在受热到一定程度又重新软化，冷却后又变硬，这种过程能够反复进行多次。如聚氯乙烯、聚乙烯、聚苯乙烯等。热塑性塑料成型过程比较简单，能够连续化生产，并且具有相当高的机械强度，因此发展很快。

热固性塑料的分子结构是体型结构，在受热时也发生软化，可以塑制成一定的形状，但受热到一定的程度或加入少量固化剂后，就硬化定型，再加热也不会变软和改变形状了。热固性塑料加工成型后，受热不再软化，因此不能回收再用，如酚醛塑料、氨基塑料、环氧树脂等都属于此类塑料。热固性塑料成型工艺过程比较复杂，所以连续化生产有一定的困难，但其耐热性好、不容易变形，而且价格比较低廉。

2、根据塑料的用途不同分为通用塑料和工程塑料

通用塑料是指产量大、价格低、应用范围广的塑料，主要包括聚烯烃、聚氯乙烯、聚苯乙烯、酚醛塑料和氨基塑料五大品种。人们日常生活中使用的许多制品都是由这些通用塑料制成。

工程塑料是可作为工程结构材料和代替金属制造机器零部件等的塑料。例如聚酰胺、聚碳酸酯、聚甲醛、ABS树脂、聚四氟乙烯、聚酯、聚砜、聚酰亚胺等。工程塑料具有密度小、化学稳定性高、机械性能良好、电绝缘性优越、加工成型容易等特点，广泛应用于汽车、电器、化工、机械、仪器、仪表等工业，也应用于宇宙航行、火箭、导弹等方面。

二、塑料的成分

我们通常所用的塑料并不是一种纯物质，它是由许多材料配制而成的。其中高分子聚合物(或称合成树脂)是塑料的主要成分，此外，为了改进塑料的性能，还要在聚合物中添加各种辅助材料，如填料、增塑剂、润滑剂、稳定剂、着色剂等，才能成为性能良好的塑料。

1、合成树脂

合成树脂是塑料的最主要成分，其在塑料中的含量一般在40％～100％。由于含量大，而且树脂的性质常常决定了塑料的性质，所以人们常把树脂看成是塑料的同义词。例如把聚氯乙烯树脂与聚氯乙烯塑料、酚醛树脂与酚醛塑料混为一谈。其实树脂与塑料是两个不同的概念。树脂是一种未加工的原始聚合物，它不仅用于制造塑料，而且还是涂料、胶粘剂以及合成纤维的原料。而塑料除了极少一部分含100％的树脂外，绝大多数的塑料，除了主要组分树脂外，还需要加入其他物质。

2、填料

填料又叫填充剂，它可以提高塑料的强度和耐热性能，并降低成本。例如酚醛树脂中加入木粉后可大大降低成本，使酚醛塑料成为最廉价的塑料之一，同时还能显著提高机械强度。填料可分为有机填料和无机填料两类，前者如木粉、碎布、纸张和各种织物纤维等，后者如玻璃纤维、硅藻土、石棉、炭黑等。

3、增塑剂

增塑剂可增加塑料的可塑性和柔软性，降低脆性，使塑料易于加工成型。增塑剂一般是能与树脂混溶，无毒、无臭，对光、热稳定的高沸点有机化合物，最常用的是邻苯二甲酸酯类。例如生产聚氯乙烯塑料时，若加入较多的增塑剂便可得到软质聚氯乙烯塑料，若不加或少加增塑剂(用量<10％)，则得硬质聚氯乙烯塑料。

4、稳定剂

为了防止合成树脂在加工和使用过程中受光和热的作用分解和破坏，延长使用寿命，要在塑料中加入稳定剂。常用的有硬脂酸盐、环氧树脂等。

5、着色剂

着色剂可使塑料具有各种鲜艳、美观的颜色。常用有机染料和无机颜料作为着色剂。

6、润滑剂

润滑剂的作用是防止塑料在成型时不粘在金属模具上，同时可使塑料的表面光滑美观。常用的润滑剂有硬脂酸及其钙镁盐等。

除了上述助剂外，塑料中还可加入阻燃剂、发泡剂、抗静电剂等，以满足不同的使用要求。

三、塑料的特性

1、塑料具有可塑性

顾名思义，塑料就是可以塑造的材料。所谓塑料的可塑性就是可以通过加热的方法使固体的塑料变软，然后再把变软了的塑料放在模具中，让它冷却后又重新凝固成一定形状的固体。塑料的这种性质也有一定的缺陷，即遇热时容易软化变形，有的塑料甚至用温度较高的水烫一下就会变形，所以塑料制品一般不宜接触开水。

2、塑料具有弹性

有些塑料也像合成纤维一样，具有一定的弹性。当它受到外力拉伸时，卷曲的分子就由柔韧性而被拉直，但一旦拉力取消后，它又会恢复原来的卷曲状态，这样就使得塑料具有弹性，例如聚乙烯和聚氯乙烯的薄膜制品。但是有些塑料是没有弹性的。

3、塑料具有较高的强度

塑料虽然没有金属那样坚硬，但与玻璃、陶瓷、木材等相比，还是具有比较高的强度及耐磨性。塑料可以制成机器上坚固的齿轮和轴承。

4、塑料具有耐腐蚀性

塑料既不像金属那样在潮湿的空气中会生锈，也不像木材那样在潮湿的环境中会腐烂或被微生物侵蚀，另外塑料耐酸碱的腐蚀。因此塑料常常被用作化工厂的输水和输液管道，建筑物的门窗等。

5、塑料具有绝缘性

塑料的分子链是原子以共价键结合起来的，分子既不能电离，也不能在结构中传递电子，所以塑料具有绝缘性。塑料可用来制造电线的包皮、电插座、电器的外壳等。

附：常用塑料的种类有：

①聚氯乙烯（PVC）

它是建筑中用量最大的一种塑料。硬质聚氯乙烯的密度为1.38～1.43g/cm3，机械强度高，化学稳定性好，使用温度范围一般在-15～+55℃之间，适宜制造塑料门窗、下水管、线槽等。

②聚乙烯（PE）

聚乙烯塑料在建筑上主要用于给排水管、卫生洁具。

③聚丙烯（PP）

聚丙烯的密度在所有塑料中是最小的，约为0．90左右。 聚丙烯常用来生产管材、卫生洁具等建筑制品。

④聚苯乙烯（PS）

聚苯乙烯为无色透明类似玻璃的塑料。 聚苯乙烯在建筑中主要用来生产泡沫隔热材料、透光材料等制品。

⑤ABS塑料

ABS塑料是改性聚苯乙烯塑料，以丙烯睛（A）、丁二烯（B）及苯乙烯（S） 为基础的三组分所组成。ABS塑料可制作压有花纹图案的塑料装饰板等

分类

* 根据热性能和加工性能

o 热塑性塑料：受热软化并可反复加热成型

+ 如聚氯乙烯塑料、聚丙烯塑料

o 热固性塑料：受热固化定型后不能再加热熔融成型

+ 如酚醛塑料、脲醛塑料

* 按用途分

o 通用塑料：产量大

+ 如聚乙烯、聚丙烯、聚氯乙烯

o 工程塑料

+ 如聚碳酸酯、聚砜、聚苯醚、聚酰胺、聚甲醛

o 特种塑料

+ 如医用塑料、导电塑料、耐高温塑料

高压纸”是塑料原型，也就相当于你有这些东西就可以做成任何你想要的东西~~~

首先你看字面意思都有所差别的啊

耐候PP肯定强调耐候

阻燃PP肯定强调的是阻燃咯

高光PP那不用说肯定是关注外观：高光的。

另外性能指标肯定有差异的。

应用当然也不一样的，打个比方，炜林纳的这些改性PP的应用就不同，不可能一个产品打天下的，需要根据不同的应用环境来选材的。

耐候PP：户外用品、室外空调机部件、户外地板，摩托车、沙滩车外部件等。

阻燃PP：线圈骨架、插线板外壳、小家电制件，微波炉、冰箱、洗衣机，电子电器产品等阻燃部件等。

高光PP：摩托车、沙滩车外壳，圆煲、方煲等小家电的面盖，饮水机、热水壶等家电产品的外壳等。

希望已回答您的问题，如果还有关于改性PP方面的问题，可以百度搜索：炜林纳改性塑料，希望对您有所帮助。

如有，请采纳，谢谢