| 中文名称 | 热镀锌钢丝 | 外文名称 | hot-dip galvanized steel wire |
|---|---|---|---|
| 别名 | 热镀锌低碳钢丝 | 工艺 | 线外退火和线内退火等 |
| 流程 | 酸洗、磷化、拔丝等 | 成分 | Fe铁,碳(C),硅(Si),锰(Mn)等 |
下表为不同行业使用的镀锌钢丝现行标准规定的尺寸允许偏差表 :
| 序号 | 尺寸允许偏差 | |||||||||||
| 公称直径mm | 桥梁缆索用 | 公称直径mm | 棉花打包用 | 公称直径mm | 通讯线用 | 公称直径mm | 铠装电缆用 | 公称直径mm | 架空绞线用 | 公称直径mm | 一般用途 | |
| GB/T 17101-2008 | GB/T 21530-2008 | GB 346-1984 | GB/T 3082-2008 | GB/T 3428-2012 | YB/T 5294-2009 | |||||||
| 1 | 5 | ±0.06 | 2.5 | ±0.05 | 1.2 | 0.06 | >0.8~1.2 | ±0.04 | >1.24~2.25 | ±0.03 | ≤0.30 | ±0.02 |
| -0.04 | ||||||||||||
| 2 | 7 | ±0.07 | 2.8 | ±0.05 | 1.5 | 0.08 | >1.2~1.6 | ±0.05 | >2.25~2.75 | ±0.04 | >0.30~1.00 | ±0.04 |
| -0.04 | ||||||||||||
| 3 | - | - | 3.2 | ±0.06 | 2 | 0.08 | >1.6~2.5 | ±0.05 | >2.75~3.00 | ±0.05 | >1.00~1.60 | ±0.05 |
| -0.04 | ||||||||||||
| 4 | - | - | 3.4 | ±0.06 | 2.5 | 0.08 | >2.5~3.2 | ±0.08 | >3.00~3.50 | ±0.05 | >1.60~3.00 | ±0.06 |
| -0.04 | ||||||||||||
| 5 | - | - | 3.75 | ±0.07 | 3 | 0.08 | >3.2~4.2 | ±0.10 | >3.50~4.25 | ±0.06 | >3.00~6.00 | ±0.07 |
| -0.04 | ||||||||||||
| 6 | - | - | 4 | ±0.07 | 4 | 0.1 | >4.2~6.0 | ±0.13 | >4.25~4.75 | ±0.06 | >6.00 | ±0.08 |
| -0.06 | ||||||||||||
| 7 | - | - | - | - | 5 | 0.1 | >6.0~8.0 | ±0.15 | >4.75~5.50 | ±0.07 | - | - |
| -0.06 | ||||||||||||
| 8 | - | - | - | - | 6 | 0.1 | - | - | - | - | - | - |
| -0.06 | ||||||||||||
| 市场价 | 信息价 | 询价 |
冷镀锌也叫电镀锌，是利用电解设备将管件经过除油、酸洗、后放入成分为锌盐的溶液中，并连接电解设备的负极，在管件的对面放置锌版，连接在电解设备的正极接通电源，利用电流从正极向负极的定向移动就会在管件上沉积一层锌，冷镀管件是先加工后镀锌。冷镀锌(电镀锌):是在电镀槽内通过电流单向性使锌逐渐镀上金属外表，生产速度慢，镀层均匀，厚度较薄，通常只有3-15微米，外观光亮、光滑、美观度高，耐腐蚀性差，一般几个月就会锈蚀。
热镀锌是由较古老的热镀方法发展而来的，自从1836年法国把热镀锌应用于工业以来，已经有一百七十年的历史了。然而，热镀锌工业是近三十年来伴随冷轧带钢的飞速发展而得到了大规模发展。
热镀锌板的生产工序主要包括:原板准备→镀前处理→热浸镀→镀后处理→成品检验等。按照习惯往往根据镀前处理方法的。
不同把热镀锌工艺分为线外退火和线内退火两大类，即湿法 (单张钢板热镀锌法)、线外退火(单张钢板热镀锌法)、热镀锌 惠林(Wheeling)法(带钢连续热镀锌法) 、线内退火 森吉米尔(Sendzimir)法(保护气体法)、 改良森吉米尔法、美钢联法(同日本川崎法)、赛拉斯(Selas)法和莎伦(Sharon)法。热镀锌:是在加热融化的锌液内浸镀，生产速度快，镀层厚但不均匀，市场允许的最低厚度45微米，最高可达300微米以上。颜色较暗，消耗锌金属多，与基体金属形成渗入层，耐蚀性好，室外环境下热镀锌可以保持几十年。
热镀锌也称热浸锌，是将钢铁工件经过除油、除锈，呈现出无污、浸润的表面，立即浸入到预先将锌加热融熔了的镀槽中去，
在工件表面形成一层锌镀层的方法。冷镀锌则是将同样经过了除油、除诱，呈现出无污、浸润的工件挂入专门的电镀槽里的阴极上，阳极用锌。接通直流电源，阳极上的锌离子向阴极迁移，并在阴极上放电，使工件镀上一层锌层的热镀锌方法。
热镀锌的镀层较厚，一般为30-60微米，镀层防腐能力较高。适合于户外工作的钢铁制件，如高速公路围栏、电力铁塔、大尺寸紧固件等较为"粗糙"的工件的长期防锈。
冷镀锌丝:是以低碳钢为芯线，通过拔丝、电镀锌工艺加工制成的金属复合材料。主要应用于制造金属丝网、高速公路护拦及建筑工程。
热镀锌丝:该产品应用优质碳素结构钢，经拉拔、热镀锌加工而成。广泛应用于制造金属丝网、高速公路护拦及建筑工程。具有镀层厚，抗腐蚀能力强、镀层牢固等特点。并可根据用户的特殊需求，按行业标准提供各种规格的镀锌丝。
相对电镀锌，热镀锌生产成本较高但对环境的影响比电镀小。
物理性能:热镀锌钢丝表面平滑、光洁、没有裂纹地、节、起刺、伤痕和锈蚀，镀锌层均匀、附着力强、耐腐蚀力持久，韧性和弹性极好。抗拉强度应在900Mpa-2200Mpa之间(丝径Φ0.2mm-Φ4.4mm)。扭转次数(Φ0.5mm)在20次以上，反复弯曲应在13次以上。
用 途:主要用于种植大棚，养殖场，棉花打包，弹簧及钢绞线，钢丝绳的制造.
Hot dip galvanized steel wire(hot-dipgalvanizedsteelwire)isa variety of high qualitycarbon steelorhighcarbon steelpickling,phosphating,drawing,and thenzinc(hot-dipplatingorcold).
So hot dip galvanizedandgalvanized ironwhat is the difference?
Cold galvanizedalso called electro-galvanized,is the use ofelectrolyticequipmentfittingsby removingoil,acid picklingsolution,theninto the composition of the zinc salt,anodeand connectedelectrolytic equipment,placingzincinpipeconnected to theopposite,anodeelectrolytic device power is turned on,thECUrrentfrom the anode to thecathodeof thEDIrectional movementwill beinpipedepositing a layer of zincplating,coolingpipe is first processedgalvanized.Cold zinc(Galvanized):isthe zincplatingmetal appearancEGRaduallythrough the currentdirectionin the plating tank,productionspeed is slow,uniform coating,thin,usually only3-15 micron,bright appearance,smooth,beautiful degreehigh,poor corrosion resistance,general a few months willrust.
Galvanizedby the more ancient hotplating method development,since 1836 the French to hotdip galvanizing applied in inDUSTry since,has been one hundred and seventy years of history.However,hot dip galvanizingindustryin recent thirty years,with the rAPId development ofcold rolled steel striphas been developed on a large scale.
Hot-dip galvanizedorhot-dip galvanizedsteel worKPIece,theafter degreasing,rust,showingno pollution,infiltration ofsurface,immediatelyimmersed inthebathof zincMeltingofheating,
Method of forminga layer of zinccoatingon the surface of workpiece.Cold galvanizingisthe sameafteroil removal,in addition to lure,showingno pollution,infiltration of theworkpiecehang into thecathodeplating tankdedicated,zincanode.DC power supply is switched on,the zinc ionon the anodeto the cathodemigration,anddischargeat the cathode,theplatinglayeronhot dip galvanizedzinc layermethod.
Hot dip galvanizedcoatingis thick,generally 30-60microns,highcorrosion resistancecoating.Iron and steelis suitable for outdoorwork,such as long-termanti-rustworkpiecehighway fence,power tower,large sizeFASteners and othermore"rough".
The production processof hot galvanized platemainly include:the original plateforhot dipplating→ of → of→aftertreATMent,finished product inspectiontreatmentbefore plating.In accordance with the habits oftentreatmentsbefore plating.
The hot dip galvanizingprocessannealingline annealingandlineintwo categories,namely,wet(LEAflets steelhot galvanizing),line annealing(leaflets steelhot galvanizing),hot galvanizedHui-lin(Wheeling)method(strip continuoushot galvanizingline annealing),Moriyoshi Mell(Sendzimir)method(protectiongas method),modified Sendzimer method,UEC(with the JapaneseKawasakimethod),Silas(Selas)method and Sharon(Sharon)method.Hot dip galvanizing:isimmersionin liquid zincmelted,fast production,coating thickness but notuniform,the minimumthickness ofmaRKEt to allow45 micron,up tOMOre than 300 microns.The darker color,the consumption ofzinc metal,infiltrationlayer is formedwith the base metal,good corrosion resistance,hot galvanizedoutdoor environmentcan keep decades.
Cold galvanized wire: lowcarbon steelas the core,through the metalcompositewire,electric galvanizEDProcessing made of.Mainlyused in the manufacture of metal mesh,Hulan and highway construction.
Hot dipped galvanized iron wire:the product structure of high-quality carbon steel,by drawing,hot-dip galvanizing processing from.Widelyused in the manufacture of metal mesh,Hulan and highway construction.With a thick coating,corrosion resistance strong,solid coatingetc..According tothe special needs of users,providinga variety of galvanized wireaccording to steel stand、 industry standards.
The relativeeffect of hot dipgalvanized,lower production cost andthe environmentthansmallelectrOPLating.
通信系统中，镀锌钢丝适用于电报、电话、有线广播 及信号传递等传输线路用。
电力系统中，因钢丝锌层质量较大、较厚，耐蚀性好，可用于线路腐蚀严重电缆 的铠装。
热镀锌钢丝网和镀锌钢丝网怎么辨别？
热镀锌是有点发黄,带花,所以人们也称其为花锌,而冷镀锌只有雪花状的白,没有别的颜色。惠民县金盛源网业有限公司的产品质量就不错，比较耐用，公司也比较诚信，而且价格也挺公道的。
国标热镀锌钢丝中c级镀锌是多少克
工频提高约10%（按长度为4尺的灯管），且自身功耗低，使灯的总输入功率下降约20%，有更佳的节能效果。（2）消除了频闪，发光更稳定。有利于提高视觉分辨率，提高功效；降低连续作业的视觉疲劳，有利于保护视...
热镀锌钢丝网和冷镀锌钢丝网的区别
热镀锌是有点发黄,带花,所以人们也称其为花锌,而冷镀锌只有雪花状的白,没有别的颜色
如何辨别热镀锌钢丝和电镀锌钢丝？
热镀锌钢丝（hot-dip galvanized steel wire）是把各种优质中碳钢或优质高碳钢经酸洗、磷化、拔丝，再镀锌（热镀或冷镀）。热镀锌工艺分为线外退火和线内退火两大类，即湿法 （单张钢...
请问大家一下60丝热镀锌钢丝网与90丝热镀锌钢丝网有什么区别？
答：网目（眼）60*60与90*90的区别吧。
热镀锌钢丝（hot-dip galvanized steel wire）是把各种优质中碳钢或优质高碳钢经酸洗、磷化、拔丝，再镀锌（热镀或冷镀）。热镀锌工艺分为线外退火和线内退火两大类，即湿法 （单张钢板热镀锌法）、线外退火（单张钢板热镀锌法）、热镀锌 惠林（Wheeling）法（带钢连续热镀锌法） 、线内退火 森吉米尔（Sendzimir）法（保护气体法）、 改良森吉米尔法、美钢联法（同日本川崎法）、赛拉斯（Selas）法和莎伦（Sharon）法。
冷镀锌也叫电镀锌，是利用电解设备将管件经过除油、酸洗、后放入成分为锌盐的溶液中，并连接电解设备的负极，在管件的对面放置锌版，连接在电解设备的正极接通电源，利用电流从正极向负极的定向移动就会在管件上沉积一层锌，冷镀管件是先加工后镀锌。冷镀锌（电镀锌）：是在电镀槽内通过电流单向性使锌逐渐镀上金属外表，生产速度慢，镀层均匀，厚度较薄，通常只有3-15微米，外观光亮、光滑、美观度高，耐腐蚀性差，一般几个月就会锈蚀。
区分：热镀锌的镀层较厚，一般为30-60微米，镀层防腐能力较高。适合于户外工作的钢铁制件，如高速公路围栏、电力铁塔、大尺寸紧固件等较为“粗糙”的工件的长期防锈。热镀锌钢丝表面平滑、光洁、没有裂纹地、节、起刺、伤痕和锈蚀，镀锌层均匀、附着力强、耐腐蚀力持久，韧性和弹性极好。抗拉强度应在900Mpa-2200Mpa之间(丝径Φ0.2mm-Φ4.4mm)。扭转次数(Φ0.5mm)在20次以上，反复弯曲应在13次以上。电镀锌厚度较薄，通常只有3-15微米，外观光亮、光滑、美观度高，耐腐蚀性差，一般几个月就会锈蚀。
热镀锌钢丝网主要用于一般建筑外墙、浇混凝土、高层住宅等，在保温系统中起着重要的结构作用，在施工时钢丝网所形成抗裂砂浆防护层可与保温材料形成的保温层一起形成外墙保温系统，有效地保护住宅的围护结构，使外界的温度变化、雨水侵蚀对建筑物的破坏大大降低，从而解决了屋面渗水、墙体开裂等顽症，延长了建筑物的寿命，也降低了维修费用。在整体性、保温性、耐久性和抗震性能方面有相当高的优越性,节能效果良好。
中文标准名称 StandardTitle in Chinese: 桥梁缆索用热镀锌钢丝
英文标准名称: Hot-dip galvanized steel wires for bridge cables
首次发布日期 FirstIssuance Date: 1997-11-11
标准状态 StandardState: 现行
复审确认日期 ReviewAffirmance Date:
计划编号 Plan No: 20062421-T-605
代替国标号 ReplacedStandard: GB/T 17101-1997
被代替国标号 ReplacedStandard:
废止时间 RevocatoryDate:
采用国际标准号 AdOPTedInternational Standard No: NF A 35-035:2001
采标名称 ADOPtedInternational Standard Name: 热镀锌或锌-铝合金预应力圆钢丝和7丝钢绞线
采用程度 ApplicationDegree: MOD
采用国际标准 AdoptedInternational Standard: 国外先进标准
国际标准分类号(ICS): 77.140.65
中国标准分类号(CCS): H49
标准类别 StandardSort: 产品
标准页码 Number ofPages:
标准价格(元) Price(￥):
主管部门 Governor: 中国钢铁工业协会
归口单位 TechnicalCommittees: 全国钢标准化技术委员会
起草单位 DraftingCommittee: 江阴华新钢缆有限公司、上海申佳金属制品有限公司、冶金工业信息标准研究院、宝钢集团上海二钢有限公司等
镀锌钢丝网主要是用镀锌的钢丝通过排列焊接加工从而制成。这种镀锌的钢丝网一般是可以被分为两种类型的，一种是热镀锌钢丝网，另一种是冷镀锌钢丝网。但不论是哪一种镀锌钢丝网，它都具有结构非常坚固结实、整体性非常强以及耐热以及耐腐蚀的性能都是很好的。在市场上这种镀锌钢丝网的价格又是多少呢
对于镀锌钢丝网，它一般是被广泛的应用在水道围栏上、建筑外墙上以及制作成各种铁栏等等。镀锌钢丝网在使用上可以节省许多的人力以及财力等。施工方便，操作简单易行。是许多行业都非常喜爱使用的产品。在市场上它的价格情况是怎样的呢在下面小编将为用户做具体介绍。
镀锌钢丝网价格
1、镀锌扎花网 钢丝轧花网 镀锌养殖网 方眼编织网
广州市越秀区达坤筛网经营部
￥1000
2、温室镀锌钢丝网 镀锌钢丝网片
安平县达瑞金属丝网制品厂
￥1600
3、热镀锌勾花网 冷镀锌菱形网 钢丝镀锌勾花网
安平县米尔丝网制品有限公司
￥400
4、冶金矿产钢丝 德阳镀锌网
四川威尔特金属丝网制品有限公司
￥204500
5、电镀锌电焊网 抹墙镀锌钢丝网 内外墙防裂网
安平县兆林丝网厂
￥100
6、焊接镀锌钢丝网
安平县齐硕丝网制品有限公司
￥200
7、矿筛网 锰钢筛网 钢丝筛网 镀锌矿筛网
山东滨州鼎秦筛网有限公司
￥35000
8、抹灰钢丝网 镀锌电焊网 工地防裂网
长沙市雨花区华海筛网经营部
￥095
9、屋面钢丝网 轻钢建筑屋顶镀锌防护钢丝网
河北硕隆金属制品有限责任公司
￥160
10、镀锌电焊网 镀锌钢丝网
北京龙福五金丝网销售中心
￥400
11、外墙保温铁丝网 镀锌铁丝网 镀锌电焊网 铁丝网
广州亨取金属制品有限公司
￥120
12、镀锌钢丝网铁轧花网
江阴利淼五金丝网制品有限公司
￥10000
13、焊接钢丝网 镀锌钢丝网
安平县汇亚丝网制品厂
￥130
14、铁丝电焊网 镀锌钢丝网 热镀锌电焊网
广州市南沙区东涌昊明金属制品厂
￥12000
15、镀锌钢丝网 轧花网
北京浩程达丝网销售中心
￥480
16、成都热镀锌轧花网厂 镀锌钢丝网 轧花网
河北创妍金属丝网有限公司
￥53200
镀锌钢丝网在市场上的应用是相对比较广泛的，它被用于建筑业、工业、农业以及采矿业上面。质量优质，使用寿命长，是比较理想的钢丝网制品。
土巴兔在线免费为大家提供“各家装修报价、1-4家本地装修公司、3套装修设计方案”，还有装修避坑攻略！点击此链接：>